EverCem Dual Cure Resin Cement Automix - MARK3


COMPARES TO: Maxcem Elite, RelyX Unicem 2 Automix, Panavia SA Cement

EverCem Dual Cure Resin Cement Automix - MARK3

SKU : 100-5385


COMPARES TO: Maxcem Elite, RelyX Unicem 2 Automix, Panavia SA Cement

$69.95

NEW from MARK3

EverCem From MARK3 is a versatile dual cure, self etch, self adhesive resin cement in an 8gm automix dual barrel syringe. It is used for cementing indirect restorations made from ceramic, composite, and metal, as well as cementing posts. It's low film thickness ensures a closer fit of the restoration while providing excelling bonding values.

Indications: indirect restorations such as, inlays, onlays, crowns, bridges, endodontic posts, zirconia crowns, implants, aluminum oxide ceramic & fiber reinforced composite posts.

Contains: (1) 8gm Automix Syringe & 6 mixing tips

3rd Quarter Promotion (ends 9.30.22)

Buy 2 EverCem Dual Cure Cements, Get 1 Free

Show More

Product Reviews


Manufacturer: MARK3

SKU: 100-5385

EverCem Dual Cure Resin Cement Automix - MARK3

EverCem From MARK3 is a versatile dual cure, self etch, self adhesive resin cement in an 8gm automix dual barrel syringe.  It is used for cementing indirect restorations made from ceramic, composite, and metal, as well as cementing posts.  It's low film thickness ensures a closer fit of the restoration while providing excelling bonding values.


Indications: indirect restorations such as, inlays, onlays, crowns, bridges, endodontic posts, zirconia crowns, implants, aluminum oxide ceramic & fiber reinforced composite posts.

Features and Benefits

  • Dual Cure - more versatile
  • no need for etching or bonding
  • easy cleanup of excess material
  • low film thickness ensuring a closer fit to the restoration
  • Radiopaque
  • Automix Delivery System

 Physical Properites

Adhesion to dentin, self-cure

22 mpa

Adhesion of zirconium oxide cylinders to dentin, self cure

18 mpa

Zirconium oxide on dentin, dual-cure

28  mpa

Adhesion to zirconium oxide, self-cure

25 mpa